Intl. Werkstoffvergleich
Werkstoff Nr. |
DIN Deutsches Institut für Normung |
AISI American Iron and Steel Institut |
AFNOR Association Francaise de Normalisation |
SS Swedish Standard |
BS British Standard |
1.4003 |
X 2 CrNi 12 |
- |
- |
- |
- |
1.4005 |
X 12 Cr S 13 |
416 |
Z 11 CF 13 |
2380 |
416 S 21 |
1.4006 |
X 10 Cr 13 |
410 |
Z 10 C 13 |
2302 |
410 S 21 |
1.4016 |
X 6 Cr 17 |
430 |
/ 8 C 17 |
2320 |
430 S 21 |
1.4021 |
X 20 Cr 13 |
420 |
Z 20 C 13 |
2303 |
420 S 37 |
1.4028 |
X 30 Cr 13 |
420 |
Z 30 C 13 |
2304 |
420 S 45 |
1.4034 |
X 46 Cr 13 |
- |
Z 40 C 14 |
(2304) |
(420 AS 45) |
1.4057 |
X 20 CrNi 17 2 |
431 |
Z 15 CN 16.02 |
2321 |
431 S 29 |
1.4104 |
X 12 CrMoS 17 |
430 F |
Z 13 CF 17 |
2383 |
(441 S 29) |
1.4105 |
X 4 CrMoS 18 |
430F |
Z 8 CF 17 |
- |
- |
1.4112 |
X 90 CrMoS 18 |
440 B |
- |
- |
- |
1.4113 |
X 6 CrMo 17 1 |
434 |
- |
- |
434 S 17 |
1.4122 |
X35 CrMo 17 |
- |
- |
- |
- |
1.4125 |
X 105 CrMo 17 |
440 C |
Z 100 CD 17 |
- |
- |
1.4301 |
X 5 CrNi 18 10 |
304 |
Z 6 CN 18.09 |
2332 |
304 S 15 |
1.4303 |
X 5 CrNi 18 12 |
305 /308 |
Z 5 CN 18.11 FF |
- |
305 S 17 |
1.4305 |
X 10 CrNiS 18 9 |
303 |
Z 8 CNF 18.09 |
2346 |
303 S 31 |
1.4306 |
X 2 CrNiS 18 9 |
304 L |
Z 2 CN 18.10 |
2352 |
304 S 11 |
1.4310 |
X 12 CrNi 17 7 |
301 |
Z 12 CN 18.08 |
2331 |
301 S 22 |
1.4313 |
X 5 Cr Ni 13 4 |
E 415 |
Z 4 CND 13.4 |
2384 |
425 C 11 |
1.4401 |
X 5 CrNiMo 17 12 2 |
316 |
Z 7 CND 17.12.02 |
2347 |
316 S 31 |
1.4404 |
X 2 CrNiMo 17 13 2 |
316 L |
Z 3 CND 18.12.02 |
2348 |
316 S 11 |
1.4435 |
X 2 CrNiMo 18 14 3 |
316 L |
Z 3 CND 18.14.03 |
2353 |
316 S 11 |
1.4436 |
X 5 CrNiM 17 13 3 |
316 |
Z 7 CND 27.05 AZ |
2343 |
316 S 31 |
1.4460 |
X 4 CrNiMo N 27 5 2 |
329 |
Z 5 CND 27.05 AZ |
2324 |
- |
1.4462 |
X 2 CrNiMoN 22 5 3 |
329A/F 51 |
Z 3 CND 22.05 |
2377 |
- |
1.4509 |
X 2 CrTiNb18 |
441 |
Z 3 CtNb18t |
- |
- |
1.4512 |
X 2 CrTi 12 |
409 |
Z 3 Ct 12 |
- |
409 S19 |
1.4539 |
X1NiCrMoCuN 25 20 5 |
- |
Z 1 NCDU 25.20 |
2562 |
- |
1.4541 |
C 6 CrNiTi 18 10 |
321 |
Z 6 CNT 18.10 |
2337 |
321 S 31 |
1.4550 |
X 6 CrNiNb 18 10 |
347 |
Z 6 CNNb 18.10 |
2338 |
- |
1.4571 |
X 6 CrNiMoTi 17 12 2 |
316 Ti |
Z 6 CNDT 17.12 |
2350 |
- |
1.4580 |
X 6 CrNiMoNb 17 12 2 |
316 CB |
Z 6 ZNDNB 17.12 |
- |
- |
1.4713 |
X 10 CrAl 7 |
- |
Z 8 CA 7 |
- |
- |
1.4742 |
X 10 CrAl 18 |
- |
Z 10 CAS 18 |
- |
- |
1.4762 |
X 10CrAl 24 |
446 |
Z 10 CAS 24 |
(2322) |
- |
1.4828 |
X 15 CrNiSi 20 12 |
309 |
Z 15 ZNS 20.12 |
- |
309 S 24 |
1.4841 |
X 15 CrNiSi 25 20 |
314 |
Z 12 CNS 25.20 |
- |
314 S 25 |